Time evaluation experiments in NMR studies of aluminosilicate solutions that transfer to the sols

Seyed Naser Azizi* , M.Mehrinejad


Zeolites crystallise from amorphous alkaline aluminosilicates under the action of heat and pressure. When an alkaline silicate solution and a specific concentration of alkaline aluminate solution are mixed, a white amorphous precipitate or colloid normally forms, the amount of colloid depending onAl and Si concentrations and the time of formation. It is possible to produce aluminosilicate solutions that remain clear for times varying fromfive minutes to several days before eventually the particles aggregate into threedimensional networks and form coagulate colloids. This work obviously has shown that the sol formation time strongly depends on the Al concentration and the temperature, while the amount of the colloidal phase depends on the Si and the alkalinity of the solution. The “colloid formation time” is defined as the time from mixing to the point when some colloid particles appeared in the solution, as judged visually and these times are listed.


மறுப்பு: இந்த சுருக்கமானது செயற்கை நுண்ணறிவு கருவிகளைப் பயன்படுத்தி மொழிபெயர்க்கப்பட்டது மற்றும் இன்னும் மதிப்பாய்வு செய்யப்படவில்லை அல்லது சரிபார்க்கப்படவில்லை

குறியிடப்பட்டது

  • CASS
  • கூகுள் ஸ்காலர்
  • ஜே கேட் திறக்கவும்
  • சீனாவின் தேசிய அறிவு உள்கட்டமைப்பு (CNKI)
  • CiteFactor
  • காஸ்மோஸ் IF
  • MIAR
  • ரகசிய தேடுபொறி ஆய்வகங்கள்
  • யூரோ பப்
  • பார்சிலோனா பல்கலைக்கழகம்
  • ICMJE

மேலும் பார்க்க

ஜர்னல் எச்-இண்டெக்ஸ்

Flyer