Preparation CuInSe2 (CIS) by arrested precipitation method as alight absorption layer of photovoltaic solar-cells

Wasan R.Saleh, OmarA.Ali


The CuInSe2 (CIS) nanocrystals are synthesized by arrested precipitation from molecular precursors are added to a hot solvent with organic capping ligands to control nanocrystal formation and growth.CIS thin films deposited onto glass substrate by spray – coating, then selenized in Aratmosphere to form CIS thin films.PVs were made with power conversion efficiencies of 0.631% as –deposited and 0.846% after selenization, for Mo coated, under AM 1.5 illumination. X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS) analysis it is evident that CIS have the chalcopyrite structure as the major phase with a preferred orientation along (112) direction and the atomic ratio of Cu : In : Se in the nanocrystals is nearly 1 : 1 : 2.


குறியிடப்பட்டது

  • CASS
  • கூகுள் ஸ்காலர்
  • ஜே கேட் திறக்கவும்
  • சீனாவின் தேசிய அறிவு உள்கட்டமைப்பு (CNKI)
  • CiteFactor
  • காஸ்மோஸ் IF
  • எலக்ட்ரானிக் ஜர்னல்ஸ் லைப்ரரி
  • டைரக்டரி ஆஃப் ரிசர்ச் ஜர்னல் இன்டெக்சிங் (DRJI)
  • ரகசிய தேடுபொறி ஆய்வகங்கள்
  • ICMJE

மேலும் பார்க்க

ஜர்னல் ISSN

ஜர்னல் எச்-இண்டெக்ஸ்

Flyer

அணுகல் இதழ்களைத் திறக்கவும்