Diffusion characteristics of the LiFePO4/C composite in an electrolyte based on LiBOB

V.A.Galaguz*, O.V.Potapenko, E.V.Panov


The behavior of a composite cathode material LiFePO4/C has been analyzed using the methods of chronopotentiometry, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The specific capacity of the LiFePO4, synthesized by the solid state method, changes from 110 to 40 mA.h/g with an increasing of the current density from 0.1 to 10C. The values of the diffusion coefficient for the lithium ions (DLi) using the CV method are 2.06.10-14 and 1.07.10-14 cm2/s for the anodic and cathodic processes, respectively. The diffusion coefficients, calculated by the impedance spectroscopy data,have been change in the range of 4.10-12 to 6.10-16 cm2/s and are in a good agreement with the cyclic voltammetry data.


குறியிடப்பட்டது

  • CASS
  • கூகுள் ஸ்காலர்
  • ஜே கேட் திறக்கவும்
  • சீனாவின் தேசிய அறிவு உள்கட்டமைப்பு (CNKI)
  • CiteFactor
  • காஸ்மோஸ் IF
  • MIAR
  • ரகசிய தேடுபொறி ஆய்வகங்கள்
  • யூரோ பப்
  • பார்சிலோனா பல்கலைக்கழகம்
  • ICMJE

மேலும் பார்க்க

ஜர்னல் எச்-இண்டெக்ஸ்

Flyer