Acetone and alcohol sensitivity of nanocrystalline nickel ferrite synthesized by sol-gel combustion technique

P.Ghosh, P.Mitra


Nanocrystalline   2 4 NiFe O was synthesized by sol-gel self-combustion technique. X-ray diffraction (XRD) was utilized for structural characterization. Broad diffraction peaks indicating smaller particle size was evident formx-ray pattern. Particle size estimated using Transmission electron microscopy (TEM) was in the range 15-25 nm. Sensitivity was found to increase with temperature before being maximum at a particular operating temperature. Significantly high sensitivity of ~88%was observed in presence of 200 ppm acetone at an operating temperature of 350oC. Maximum sensitivity of ~76% was observed for 200 ppm alcohol at an operating temperature of 300oC.


குறியிடப்பட்டது

  • CASS
  • கூகுள் ஸ்காலர்
  • ஜே கேட் திறக்கவும்
  • சீனாவின் தேசிய அறிவு உள்கட்டமைப்பு (CNKI)
  • CiteFactor
  • காஸ்மோஸ் IF
  • டைரக்டரி ஆஃப் ரிசர்ச் ஜர்னல் இன்டெக்சிங் (DRJI)
  • ரகசிய தேடுபொறி ஆய்வகங்கள்
  • அறிஞர் கட்டுரை தாக்கக் காரணி (SAJI))
  • ICMJE

மேலும் பார்க்க

ஜர்னல் ISSN

ஜர்னல் எச்-இண்டெக்ஸ்

Flyer

அணுகல் இதழ்களைத் திறக்கவும்